Description
Translucent Orange PETG | 1 kg of FDM filament | Prints at 50-250 mm/s | 52±1 MPa tensile strength | Suits all FDM 3D printers
Quick Specs
- Print in vivid Translucent Orange (#FF8F1C) for light-catching, eye-catching models
- Enjoy sturdy PETG parts with a tensile strength of 52±1 MPa
- Achieve fast results with printing speeds from 50-250 mm/s
- Get flowing, consistent extrusion with a melt flow index of 25±3 g/10 min
- Use it on all FDM 3D printers on the market
Bring Your Prints to Life in Translucent Orange
The ANYCUBIC PETG Filament in Translucent Orange is made for makers who want functional prints with real visual impact. The Translucent Orange colour (#FF8F1C) gives models a vivid, see-through look, which suits prototypes, covers, display pieces and creative projects. Each spool holds 1 kg of PETG, so you have plenty of material for repeated prints. It is also designed to work with all FDM 3D printers on the market, which makes it an easy addition to your existing setup.
Strong, Flexible Parts You Can Rely On
Tired of prints that crack the moment they are put to work? This PETG filament is rated for a tensile strength of 52±1 MPa and a bending strength of 80±2 MPa, so your parts can handle everyday handling and load. An elongation at break of 13±1% gives the material some flex before it fails, while an Izod impact strength of 45±2 kJ/m² (X-Y) helps it cope with knocks. A Young's modulus of 1850±100 MPa and a bending modulus of 2000±50 MPa describe a stiff, dependable material for practical parts.
Smooth Extrusion and Fast Printing
With a melt flow index of 25±3 g/10 min (250℃/2.16kg), this filament is formulated to flow consistently through the nozzle. It prints at a nozzle temperature of 230-250 ℃ and a bed temperature of 60-70 ℃, and supports printing speeds from 50 to 250 mm/s. That range lets you choose between slower, detail-focused prints and faster production runs. The density of 1.23 g/cm³ is a useful reference when you estimate material use for your projects.
Heat Behaviour and Storage Care
Knowing a material's thermal limits helps you pick the right use for each part. This PETG has a Vicat softening temperature of 72 ℃ and a heat deflection temperature of 69 ℃ (0.45MPa), so you can judge where it suits your application. If your filament has absorbed moisture, drying at 55-65 °C for 6-8 hours helps you get it back to print-ready condition. Follow these guidelines to get consistent, good-looking results from your Translucent Orange PETG spool.
Features
- Translucent Orange (#FF8F1C) colour for vivid, light-catching prints
- PETG FDM filament supplied on a 1 kg net weight spool
- Tensile strength of 52±1 MPa and bending strength of 80±2 MPa for durable parts
- Izod impact strength of 45±2 kJ/m² (X-Y) and 13±1% elongation at break for toughness
- Melt flow index of 25±3 g/10 min (250℃/2.16kg) for consistent flow
- Prints at 50-250 mm/s with a 230-250 ℃ nozzle and 60-70 ℃ bed
- Heat deflection temperature of 69 ℃ (0.45MPa) and Vicat softening temperature of 72 ℃
- Compatible with all FDM 3D printers on the market
- Drying guidance of 55-65 °C for 6-8 h to keep filament print-ready
Specifications
- Filament Material: PETG
- Density: 1.23 g/cm³
- Melt Flow Index: 25±3 g/10 min (250℃/2.16kg)
- Tensile Strength: 52±1 MPa
- Young's Modulus: 1850±100 MPa
- Elongation at Break: 13±1%
- Bending Strength: 80±2 MPa
- Bending Modulus: 2000±50 MPa
- Izod Impact Strength: 45±2 kJ/m² (X-Y)
- Melting Temperature: 130 ℃
- Vicat Softening Temperature: 72 ℃
- Heat Deflection Temperature: 69 ℃ (0.45MPa)
- Nozzle Temperature Range: 230-250 ℃
- Bed Temperature Range: 60-70 ℃
- Printing Speed Range: 50-250 mm/s
- Drying Temperature & Time: 55-65 °C, 6-8 h
- Compatible Printers: All FDM 3D printers on the market
- Material Type: FDM Filament
- Colour: Translucent Orange (#FF8F1C)
- Net Weight: 1 kg